Appearance (Raw) | Turbid |
Mechanical Properties | High Strength |
Appearance (Finished Product) | Glossy |
Moulding | SMC/BMC |
Main Application | Water Tank Panel, Industrial Parts |
Specific Weight @25⁰C | @25⁰C | 1.10 |
Acid Value | – | 16 – 24 mgKOH/g |
Viscosity | @25⁰C | 1300 – 1700 mPa.s |
Solid Content | – | 61 – 67 % |
Reactivity (SPI) | Test Temperature | 82.2℃ |
Catalyst System | 1.0 pbw BPO | |
Gel Time | 9 ~ 11 min | |
Peak Exothermic Temperature | 215 ~ 275℃ |
Mechanical Properties | Barcol Hardness (934-1) | 50 | |
Tensile ASTM D 638 | Tensile Strength | 55 MPa | |
Tensile Modulus | 3000 MPa | ||
Elongation at Break | 2.3 % | ||
Flexural ASTM D 790 | Flexural strength | 100 MPa | |
Flexural modulus | 3100 MPa | ||
Thermo Mechanical Properties | HDT ASTM D 648 | 120℃ | |
Post cure | Room temp.*6hrs, 80℃*2hrs and 120℃*1hr | ||
Post cure | Room temp.*6hrs, 80℃*2hrs & 120℃*1hr & 150℃*1hr | ||